Effect of Homogenization Treatment on Microstructure and Property of Al-B Electrician Round Rod
Ting-yi Lin, Xiao-yan Zhang, Xin Huang, Xiang-peng Gong, Jun-jie Zhang
Available Online March 2016.
- https://doi.org/10.2991/icmmct-16.2016.185How to use a DOI?
- Al electrician round rod, homogenization, electrical conductivity, tensile strength
- The effects of homogenization treatment on the electrical conductivity, tensile strength and microstructure of Al-B electrician round rod were investigated by means of tensile test, optical microscopy(OM), scanning electron microscopy (SEM), energy dispersive spectroscopy(EDS). The results indicate that during homogenization the grain boundary of samples became thinner, microstructure was more compact and well-distributed. As-cast Al electrician round rod has favorable comprehensive properties under homogenization at 430â„ƒ for 3 h, the electrical conductivity and tensile strength reach to 58.1%IACS and 100MPa, respectively. Compared to the sample without homogenization, the electrical conductivity increased by 2.1%IACS in the case of tensile strength was not reduced. After 83% rolling processing of specimen with better comprehensive performance, the electrical conductivity and tensile strength of samples reach to 55.24%IACS and 209MPa, respectively.
- Open Access
- This is an open access article distributed under the CC BY-NC license.
Cite this article
TY - CONF AU - Ting-yi Lin AU - Xiao-yan Zhang AU - Xin Huang AU - Xiang-peng Gong AU - Jun-jie Zhang PY - 2016/03 DA - 2016/03 TI - Effect of Homogenization Treatment on Microstructure and Property of Al-B Electrician Round Rod BT - Proceedings of the 2016 4th International Conference on Machinery, Materials and Computing Technology PB - Atlantis Press SP - 929 EP - 933 SN - 2352-5401 UR - https://doi.org/10.2991/icmmct-16.2016.185 DO - https://doi.org/10.2991/icmmct-16.2016.185 ID - Lin2016/03 ER -