Study on Preparation and Properties of ZrO2/Sepiolite composite
- 10.2991/icaemt-15.2015.117How to use a DOI?
- sepiolite; zirconium dioxide; specific surface area; thermal stability
Sepiolite as catalyst carrier material, now commonly used in low temperature, for high temperature applications was very rare. ZrO2/sepiolite precursor was prepared by Chemical precipitation method, catalyst coating material was prepared at 600 , the samples were aged at 1000 . The powders with and without aging were characterized by means of BET (BET surface area), TG, XRD and SEM. The effect of acidification time on sepiolite surface area and the influences of Lanthanum adding, mass ratio of ZrO2 and sepiolite on the composite properties were studied. The results indicate that after acidification 18h sepiolite surface area up to 148.12 m2•g-1. When added 6 Wt.% La, mass ratio of ZrO2 and sepiolite was 3:2, ZrO2/ sepiolite catalyst coating composite surface area is maximum, reach to 95.7553 m2•g-1, with the 1000 aging, the specific surface area still up to 55.7553 m2•g-1, besides, it has good thermal stability. Compared with the specific surface area of sepiolite with high temperature treatment, this catalyst carrier coating composite improved significantly.
- © 2015, the Authors. Published by Atlantis Press.
- Open Access
- This is an open access article distributed under the CC BY-NC license (http://creativecommons.org/licenses/by-nc/4.0/).
Cite this article
TY - CONF AU - Chenyi Dai AU - Ying Liu AU - Xiaogang Yao AU - Xiuchen Zhao PY - 2015/08 DA - 2015/08 TI - Study on Preparation and Properties of ZrO2/Sepiolite composite BT - Proceedings of the 2015 International Conference on Advanced Engineering Materials and Technology PB - Atlantis Press SP - 605 EP - 610 SN - 2352-5401 UR - https://doi.org/10.2991/icaemt-15.2015.117 DO - 10.2991/icaemt-15.2015.117 ID - Dai2015/08 ER -